Our products are manufactured to meet a varied range of criteria. Typical properties designed into our range of polymers include;
Heat resistance, impact resistance, reinforcement, UV resistance, flame retardants and chemical resistance. All our compounds can be complemented with special appearance effects.
RoHS and WEE compliance are available as standard across our range of products and we offer a comprehensive range of packaging and delivery options.
| Percom PP | |||||||||||
| Injection Moulding Compounds | |||||||||||
| Polymers Available | MFI Range | Heat Stabilised | UV | Impact Modified | Antimicrobial | Std Colour | Effect Colour | Scratch Resistant | Metal Deactivated | Nucleated | Antistatic |
| Homopolymer | 0.3 - 50 | O | O | O | O | O | O | O | O | O | |
| Coplolymer | O | O | O | O | O | O | O | O | O | ||
| Random Copolymer | O | O | O | ||||||||
| Filled | O | O | O | O | O | O | O | O | O | O | |
| FR | O | O | O | O | O | O | O | O | |||
| Percom PP | |||||||||||
| Glass Coupled Moulding Compounds | |||||||||||
| Key Properties | Standard | Units | DHG20 | DHG30 | DHG40 | DCG20 | DCG30 | KHG20B | KCG30B | ||
| MFI | ISO1133 | cm3/10min | 1.5 | 2.5 | 2.5 | 2.5 | 2.5 | 8 | 12 | ||
| Izod Notched Impact | ISO 180 1A | KJ/m2 | 12 | 12 | 13 | 12 | 12 | 6 | 5 | ||
| Tensile Strength | ISO 527-2 | Mpa | 80 | 93 | 106 | 70 | 75 | 35 | 35 | ||
| Flexural Modulus | ISO 178 | MPa | 4600 | 5600 | 7800 | 3700 | 5100 | 1800 | 2000 | ||
| HDT A 0.45 MPa | ISO 75-2 | C | 150 | 151 | 155 | ||||||
| HDT B 1.8 MPa | ISO 75-2 | C | 120 | 123 | 126 | ||||||
| FR | UL 94 | Class | HB | HB | HB | HB | HB | V2 | V2 | ||
| Data Sheet | Data Sheet | Data Sheet | Data Sheet | Data Sheet | Data Sheet | Data Sheet | Data Sheet | ||||
| Comment | Current products available with a range of mfi values | ||||||||||
| Percom PP | |||||||||||
| Mineral Filled Moulding Compounds | |||||||||||
| Key Properties | Standard | Units | KHT10 | KHT20 | KHT30 | KHT40 | KCT10 | KCT20 | KCT30 | KCT40 | |
| MFI | ISO1133 | cm3/10min | 9 | 9 | 9 | 9 | 9 | 9 | 9 | 9 | |
| Izod Notched Impact | ISO 180 1A | KJ/m2 | 3 | 3 | 3 | 3 | 8 | 6 | 6 | 5 | |
| Tensile Strength | ISO 527-2 | Mpa | 27 | 30 | 33 | 34 | 29 | 30 | 31 | 32 | |
| Flexural Modulus | ISO 178 | MPa | 2300 | 3000 | 4000 | 4500 | 2100 | 2400 | 3200 | 4150 | |
| HDT A 0.45 MPa | ISO 75-2 | C | 115 | 120 | 126 | 130 | 100 | 115 | 125 | 130 | |
| HDT B 1.8 MPa | ISO 75-2 | C | 82 | 85 | 87 | 88 | 78 | 84 | 86 | 88 | |
| FR | UL 94 | Class | HB | HB | HB | HB | HB | HB | HB | HB | |
| Data Sheet | Data Sheet | Data Sheet | Data Sheet | Data Sheet | Data Sheet | Data Sheet | Data Sheet | Data Sheet | |||
| Comment | Current products available with the following nominal mfi values 3(D), 5(F), 9(K), 18(P), 25(R) | ||||||||||
| Percom PP | |||||||||||
| Flame Retardant Moulding Compounds | 960GW / V2 | VO MF | VO MF | VO MF | VO GF | ||||||
| Key Properties | Standard | Units | XYH16FR | XG1229T15 | XG1198T10 | XG1198T20 | XG1248G20 | ||||
| MFI / 230 @ 2.16 | ISO1133 | cm3/10min | Range | 10 | 10 | 10 | 3.5 | ||||
| Izod Notched Impact | ISO 180 1A | KJ/m2 | 9 | 14 | 7 | 7 | 10 | ||||
| Tensile Strength | ISO 527-2 | Mpa | 27 | 20 | 20 | 20 | 68 | ||||
| Flexural Modulus | ISO 178 | MPa | 1300 | 2250 | 2250 | 2600 | 4200 | ||||
| HDT A 0.45 MPa | ISO 75-2 | C | 85 | 94 | 97 | 97 | 150 | ||||
| HDT B 1.8 MPa | ISO 75-2 | C | 54 | 72 | 75 | 80 | 135 | ||||
| GW | IEC695-2-1 | C | 960 @ 1mm | 960 @ 2mm | 960 @ 2mm | 960 @ 2mm | 960 @ 2mm | ||||
| FR | UL 94 | Class | V2 | V0 @ 1.6mm | V0 @ 1.6mm | V0 @ 1.6mm | V0 @ 3.2mm | ||||
| Data Sheet | Data Sheet | Data Sheet | Data Sheet | Data Sheet | Data Sheet | ||||||
| X - X = A to Z, represents the melt flow index, A low melt flow, Z high melt flow | |||||||||||
| Y - Y = A,B,C,D represents the content of talc in the compound. A=0% talc, B=10% talc, C=15% talc, D=20% talc | |||||||||||